Equilibrium Moisture Content and Dimensional Stability of Flattened Bamboo Softened by High Temperature Saturated Steam
-
摘要: 为毛竹展平板干燥终含水率的确定，养生、平衡、仓储环境参数设定等提供理论依据，对两种不同温度高温饱和蒸汽软化毛竹展平板的解吸、吸湿平衡含水率和体积干缩、湿胀率进行测定，研究结果表明：（1）在高温饱和蒸汽软化和展平的共同作用下，毛竹展平板的解吸和吸湿平衡含水率均明显低于同等环境下的木材平衡含水率，160℃和180℃高温蒸汽软化展平板的干燥终含水率为同环境状态时木材平衡含水率的65.17%和62.40%为宜，在通风良好的条件下材料养生、平衡时间250-350h为宜；（2）180℃软化展平板的吸湿和解吸平衡含水率均低于160℃的，软化温度越高，吸湿和解吸平衡含水率越低；（3）180℃软化展平板的体积干缩率和湿胀率均低于160℃的，较高的软化温度有利于提高展平板的尺寸稳定性。Abstract: In order to explore the water content, maintenance and balancing, and storage of flattened bamboo for the purpose of theoretical guidance to manufacture, the equilibrium moisture content in the absorption and desorption process of flattened bamboo softened by saturated steam at different temperature, and their volume shrinkage and expansion rates have been investigated. The results showed that (1) with the coordination effect of high temperature saturated steam softening and flattening influence, the equilibrium moisture content in the absorption and desorption process of flattened bamboo were significantly lower than that of wood counterparts under the same conditions. The optimal equilibrium moisture content of flattened bamboo softened at 160℃ and 180℃ was 65.17% and 62.40%, respectively, when in good ventilated condition, the appropriate time for curing and maintenance of bamboo material was set at 250-350 h; (2) equilibrium moisture content in the absorption and desorption process of bamboo flattening at 180℃ was higher than that at 160℃, the higher softening temperature, the lower equilibrium moisture content in the absorption and desorption process of the flattened bamboo; (3) volume shrinkage and expansion rates of flattened bamboo softened by saturated steam at 180℃ were lower than that of softened at 160℃, which demonstrated that high softening temperature contribute to the better dimensional stability.
-
[1] 张齐生.竹类资源加工及其利用前景无限[J].中国林业产业,2007(3):22-24. [2] 国家林业局.全国竹产业发展规划(2013-2020)[R].2013. [3] 徐明,任海青,徐金梅,等.中国近五年竹材加工利用研究进展及展望[J].世界林业研究,2008,21(1):61-67. [4] 张齐生.竹类资源加工的特点及其利用途径的展望[J].中国林业产业,2004(1):9-11. [5] 黄梦雪,张文标,张晓春,等.竹材软化展平研究及其进展[J].竹子研究汇刊,2015,34(1):31-36. [6] 吴一飞,毛竹材无裂纹软化展平工艺研究[D].南京:南京林业大学硕士论文,2018. [7] 南博,王书强,李延军,等.高温热处理对毛竹材颜色和平衡含水率的影响[J].浙江林业科技,2015,35(3):57-60. [8] 孙润鹤,刘元,李贤军,等. 高温热处理对竹束颜色和平衡含水率的影响[J].中南林业科技大学学报,2012,32(9):138-141. [9] 张晓春,徐君庭,蒋身学,等.热处理重组竹材的吸湿平衡含水率和尺寸稳定性[J].木材工业.2016,(5).35-37. [10] 邵迎涛, 王新洲, 李延军,等.高温饱和蒸汽软化工艺对竹展平板物理力学性能的影响[J].竹子学报.2018,37(2).23-27. [11] 姜志宏,孟志康,张永良.毛竹的含水率[J].竹子研究汇刊;1995,14(2):58-67. [12] 姜志宏,俞友明,金巧飞,等.竹质人造板的平衡含水率[J].竹子研究汇刊,1996,15(3):45-52. [13] 张亚梅.热处理对竹材颜色及物理力学性能影响的研究[D].北京:中国林业科学硕士论文,2010. [14] 林勇,沈钰程,于利,等. 高温热处理竹材的物理力学性能研究[J].林业机械与木工设备,2012,40(8):22-24. [15] 李任,黄荣凤,高志强,等.预热温度对毛白杨压缩木材颜色及其回弹的影响[J].林产工业,2019,46(5):17-21. [16] 赵璐,薛静,贾文,等.竹材的氟硼酸钠/DDAC改性与性能表征[J].林产工业.2019,56(12):24-29,51. [17] 张芊,梁广元,黄梦雪,等.毛竹筒展平板微观结构和基本性能初步研究[J].世界竹藤通讯,2016,14(6):11-13,18. [18] 余立琴. 热处理对竹材线性干缩率的影响[J].林业机械与木工设备,2013,41(7):32-33,37. [19] 王建和,孙丰文,张齐生.竹片胀缩性能的初步研究[J].竹子研究汇刊;1993,12(1):39-46. -
点击查看大图
计量
- 文章访问数: 509
- HTML全文浏览量: 89
- PDF下载量: 72
- 被引次数: 0
下载: